Transcript Laminated plates - University of Kentucky College of

+
Laminated plates
+
definitions

Unidirectional: orientation direction is identical for all
laminates

Angle-ply:



Cross ply:



Fiber orientation alternates between +theta to –theta from the
stress normal
…/q/-q/q/-q/…
Fibers in alternating plies are at right angles to each other
…/0/90/0/90/…
Symmetric: fiber orientation in the stack is symmetric about
the center line of the laminate
+
Symmetric laminate examples

7 ply stack:

This stack is symmetrical about
the centerline of the 4th ply

The stack order is a ‘mirror’
reflection about the centerline

We will need the average height
of the ply above the centerline.
Ply #
orientation
Distance
above
ctrln
1
0
+3
2
+45
+2
3
-45
+1
4
90
0
5
-45
-1
6
+45
-2
7
0
-3
+
Symmetric laminate examples

8 ply stack:

This stack is symmetrical about
the interface between ply 4 and
ply 5

The stack order is a ‘mirror’
reflection about the centerline

We will need the average height
of the ply above the centerline.
Ply #
orientation Distance
above
ctrln
1
0
+3½h
2
+45
+2 ½ h
3
-45
+1½h
4
90
+½h
5
90
-½h
6
-45
-1½h
7
+45
-2½h
8
0
-3 ½ h
+
Antisymmetric

Ply orientation is antisymmetric about the centerline of the
laminate

For each ply with fiber orientation angle, q, above the
midplane, this is a ply of fiber orientation angle, –q, with
identical material and thickness and equal distance below
the midplane
 q(z)=-q(-z)
 q/-q/q/-q
is antisymmetric
 q/-q/-q/q is symmetric
+
Unsymmetric laminate

Unsymmetric: q1/q2/q3; random placement of angles

Quasi-isotropic laminate: equal angles between adjacent
lamina, increment is p/n

+60/0/-60

+45/0/-45/-90

0/+60/-60

0/+45/-45/90
+
Quasi-isotropic laminates


Quasi-isotropic laminate: equal angles between adjacent
lamina, increment is p/n

+60/0/-60

+45/0/-45/-90

0/+60/-60

0/+45/-45/90
A common quasi-isotropic symmetrical stacking sequence is:
[0/±45/90]s
+
Code examples

[0/45/90]s: 1st angle is for the outermost ply, last angle is for
the innermost ply; s subscript means symmetrical

The bar over 90 indicates that the plan of symmetry passes
midway through the thickness of the 90 degree laminate

±45 implies adjacent +45 and -45 degrees laminates

04: four adjacent zero degree plies

(±45)2: two grouped, adjacent ±45 degree plies
+
In-class examples

Sketch the following:

[0/45/90]s

[0/-45/90]s

[0/±45/90]s
Young B35 classroom (30 student seats and 1 teacher station)
Thursday 4/3 3:30pm-4:45pm
Thursday 4/10 3:30pm-4:45pm
Peggy M. Akridge
Manager, Student Computing Services
UK Analytics and Technologies
University of Kentucky
+
Lamination theory
+
Step-by-step procedure
1.
Calculate stiffness matrices for the laminate
2.
Calculate the midplane strains and curatures for the
laminate due to specific applied forces
3.
Calculate in-plane stresses, exx, eyy, gxy, for each lamina
4.
Calculate in-plane strains, sxx, syy, txy, for each lamina
+
Assumptions

Laminate is thin, wide: w>>t

Perfect interlaminar bonds

Strain distribution in the thickness direction is linear

All laminas are macroscopically homogeneous and behave
linearly elastically
+
Laminate strains

Since strain distribution in z direction is linear,
e xx = e + z × kxx
0
xx
• Geometric midplane = xy axes, z axis
defines thickness direction
• Total laminate thickness = h
• Thickness of various lamina are ti
• Total lamina = N
e yy = e + z × kyy
0
yy
g xy = g + z × kxy
0
xy
+
Laminate strains

Since strain distribution in z direction is linear,
e xx = e + z × kxx
0
xx
•
•
•
•
e0ii = midplane normal strains
g0xy = midplane shear strain
Kii bending curvatures of laminate
Kxy = twisting curvature of laminate
e yy = e + z × kyy
0
yy
g xy = g + z × kxy
0
xy
+
e xx = e xx0 + z × kxx
e yy = e yy0 + z × kyy
g xy = g xy0 + z × kxy
+
+
+