Transcript 슬라이드 1
Characteristics of Starsen PPS XP-2140MX ASTM data Properties Standard Unit XP-2140MX GF40% General General information Physical properties Density ASTM D-792 - 1.66 - % 40 Water absorption, 24h/23oCoC D-570 % 0.02 Mold shrinkage (MD/TD) D-955 % 0.25 / 1.0 Tensile strength D-638 Mpa Kg/cm2 psia 180 1,800 26,000 Tensile elongation at break D-638 % 2.2 Flexural strength D-790 Mpa Kg/cm2 psia 250 2,500 36,000 Flexural modulus D-790 Mpa Kg/cm2 psia 13,000 133,000 1,886,000 IZOD impact strength (Notched) D-256 J/m Kg·cm/cm ft·lb/in 100 10 1.9 IZOD impact strength (Unnotched) D-256 J/m Kg·cm/cm ft·lb/in 500 50 9.0 oC oF 270 518 Filler content Mechanical properties at 23oC Thermal properties HDT, 1.82Mpa D-648 Coefficient of linear expansion D-696 cm/cm oC 2.0×10-5 UL flammability at 0.8mm UL-94 - V-0 oC 300 ~ 340 572 ~ 644 Processing condition Cylinder temperature - Mold temperature - These properties represent standard natural color specimens oF oC oF 120 ~ 150 248 ~ 302 Characteristics of Starsen PPS XP-2140MX Properties Standard Unit ISO data XP-2140MX GF40% General General information Physical properties Density ISO 1183 - 1.66 - % 40 ISO 62 % 0.02 - % 0.25 / 1.0 Tensile strength ISO 527 Mpa 190 Tensile elongation at break ISO 527 % 2 Flexural strength ISO178 Mpa 260 Flexural modulus ISO 178 Mpa 14,500 IZOD impact strength (Notched) ISO 180/1A KJ/m2 10 IZOD impact strength (Unnotched) ISO 180/1U KJ/m2 45 HDT, 1.82Mpa ISO 75-2 AF oC 270 Coefficient of linear expansion ISO 11359-2 cm/cm oC 2.0×10-5 UL-94 - V-0 Cylinder temperature - oC 300 ~ 340 Mold temperature - oC 120 ~ 150 Filler content Water absorption, 24h/23oCoC Mold shrinkage (MD/TD) Mechanical properties at 23oC Thermal properties UL flammability at 0.8mm Processing condition These properties represent standard natural color specimens