Transcript LDC borstplätering LDC Portable Electroplating 1. Cold process: used at room temperature, no stress or adjustments because of termal distorsion. 2.

LDC borstplätering
LDC Portable Electroplating
1. Cold process: used at room temperature, no stress or adjustments because of
termal distorsion.
2. To tolerance: normally no machining required
3. Quick metal build-up: 0,05 mm in 10-15 min.
4. Plating: on all conductive materials, cast iron, stainless, mild steel, copper,
chrome etc
5. Dense deposits: no or very little porosity in most coatings
6. Many differens metals: nickel, gold, silver, copper, cobolt, zinc and alloys.
7. Excellent bonding: molecular bonding results in very god adhesion, all coatings
can be machined, ground or polished.
8. Mobile equipment: the repair can be done on site
www.ldc-brushplating.com
2
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
On site repair
of the
crankshaft in
a conversion
press.
www.ldc-brushplating.com
3
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Damaged /worn
flywheel bearing
areas on the
crankshaft in a
conversion press.
www.ldc-brushplating.com
4
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Prepare and
masking off
surrounding
areas.
www.ldc-brushplating.com
5
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Plating
procedure
going on .
www.ldc-brushplating.com
6
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Damaged
bearing journal
plated to size.
www.ldc-brushplating.com
7
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Crankshaft is
finished and
the original
tolerances and
measurements
are obtained.
Ready to
assemble the
flywheel .
www.ldc-brushplating.com
8
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Repair on site .
Lower bed die
in a conversion
press with local
wear damages
www.ldc-brushplating.com
9
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Plated/repaired
damage on the
lower bed die.
LDC-2904
copper hi-speed
HB250 were
used to fill the
damage up . Top
coated with
LDC-2807 Nickel
acid for wear
and corrosion
protection.
www.ldc-brushplating.com
10
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Repair on site .
Lower bed die in
a conversion
press with local
wear damages
www.ldc-brushplating.com
11
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Damaged area
in the lower bed
die.
www.ldc-brushplating.com
12
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
One worn out
slide. There are
damages from
the pistons and
micro
vibrations. And
causes oil
leaking.
www.ldc-brushplating.com
13
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Damaged area
inside the slide
www.ldc-brushplating.com
14
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
The damages is
being plated
with a hard
copper of 250
Brinell and
grinded to
original
tolerances.
www.ldc-brushplating.com
15
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Area has now a
new top coating
with a nickel
with a hardness
of 400 brinell
and also gives a
excellent
protection from
new damages.
www.ldc-brushplating.com
16
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Plating is now
finished and the
slide is ready for
assembly.
www.ldc-brushplating.com
17
LDC borstplätering
Tele: + 46 248 174 40 E-mail: [email protected]
Oil leakage
from scratched
and damaged
main pistons
brush plated
on site.
www.ldc-brushplating.com
18