Transcript Polymer Process Engineering

Course overview
7/20/2015
Chapter 1. Primer/introduction
1
Course webpage
• http://courses.engr.uky.edu/CME/mse404g/
• This contains:
– Course material by year (Powerpoints, other material
grouped by chapter, course syllabus, special projects/lectures, material
to prep for the final,…)
– A study guide for each chapter
– Each chapter (text pdfs)
7/20/2015
Chapter 1. Primer/introduction
2
Chapter 1
•
•
•
•
Download the text
Download the study guide
Assignments will be posted here
I suggest that you read the 1st chapter prior to
Thursday
7/20/2015
Chapter 1. Primer/introduction
3
Chapter 1
• Educational outcomes: what you should be
able to do based on the material in Chapter 1
• Nomenclature: list of terms you should be
able to define
• Critical concepts: things you should know
based on this chapter
7/20/2015
Chapter 1. Primer/introduction
4
Educational outcomes
• Be able to define all the terms listed
• Understand and apply the critical concepts
• Chapter 1 is quick summary of major points
about polymeric materials [if you don’t remember
anything else, remember this…]
7/20/2015
Chapter 1. Primer/introduction
5
Polymer Process Engineering
Chapter 1. Primer
7/20/2015
Chapter 1. Primer/introduction
6
Fundamental concepts + language
Nomenclature
Chemical bonding, chemical interactions, entanglements
Molecular weight
Thermal transitions
PRIMER
7/20/2015
Chapter 1. Primer/introduction
7
Berzelius (1883) – Poly (many) + mer (unit)
Polystyrene polymerized in 1938; polyethylene glycol made in 1860s
Early polymer products were based on cellulose- gun cotton = nitrated
cellulose
WHAT IS A POLYMER?
7/20/2015
Chapter 1. Primer/introduction
8
A polymer is…
• Long chain molecule, often based on organic
chemical building blocks (monomers)
• Long molecules (Mw ~100,000 Da) have solidlike properties
• The chain may be amorphous (no regular
structure), crystalline (a regular repeating
structure), crosslinked,…
• Dendrimers and oligomers have different
properties
7/20/2015
Chapter 1. Primer/introduction
9
Chemical structure
Chain morphology – constitution, configuration, conformation
Degree of polymerization = number of repeating units
Building block sources – hydrocarbons, renewable materials
HOW DO YOU BUILD A MOLECULE?
7/20/2015
Chapter 1. Primer/introduction
10
Building blocks
• 5% of petroleum goes
into polymers
• Sustainable use is
possible
• Energy recovery is
possible if solid
polymers are
combusted
7/20/2015
Type
C
H
O
gas
NG
3
1
0
liquid
Crude
6
1
0
solid
Coal
14
1
0
Renew- cellulose
able
6
1
5.3
Hemicellulose
6
1
8
lignin
6.8
1
3
protein
Chapter 1. Primer/introduction
11
‘Building’ methods
Chain (addition)
• Example – polyethylene (PE)
from ethylene
• Small number of reacting
chains at any one time,
which can grow into long
molecules prior to
termination
• Long reaction times needed
to achieve high conversions
7/20/2015
Step (condensation)
• Example – poly(ethylene
terephthalate) (PET) from
terephthalic acid and
ethylene glycol
• Endgroups react to build the
chain; long reaction times
needed to achieve high
polymer
Chapter 1. Primer/introduction
12
Multiple building blocks
• Copolymers, terpolymers, …
• Using multiple building blocks leads to
polymers with intermediate properties or
unique properties compared to the
homopolymers
7/20/2015
Chapter 1. Primer/introduction
13
Several copolymer
configurations
7/20/2015
Chapter 1. Primer/introduction
14
Chain configurations
• Linear – repeating units are aligned
sequentially
• Branched – large segments ‘branch’ off the
main chain/carbon backbone
• Crosslinked/network – chemical crosslinks
between chains add mechanical strength
• EXAMPLES?
7/20/2015
Chapter 1. Primer/introduction
15
Multiphase systems
• Composites
– Structural
– Random
– Other
– Nanocomposites
• Blends
– Dispersed lamellae, cylinders, spheres
7/20/2015
Chapter 1. Primer/introduction
16
Structure – chemical, configuration
solid performance (mechanical + thermal properties)
other
HOW DO WE CLASSIFY POLYMERS?
7/20/2015
Chapter 1. Primer/introduction
17
Mechanical + Thermal
• Thermoplastic – solidified by cooling and
reheated by melting
• Thermosets – retain their structure when
reheated after polymerization (usually
crosslinked)
• Elastomers – rubbers, deform readily with
applied force
• Thermoplastic elastomers
• other
7/20/2015
Chapter 1. Primer/introduction
18
Very few commercial products are ‘pure’
MWD – molecular weight distribution
additives
WHAT IS IN A COMMERCIAL
PRODUCT?
7/20/2015
Chapter 1. Primer/introduction
19
Polymers vs. metals
Why do we use
polymers?
7/20/2015
Chapter 1. Primer/introduction
20
Polymeric materials
• Compete well on a strength/weight basis
• Easy to form into 3D shapes
• Creep under load is usually poor; this behavior
is usually corrected by adding fillers or fibers
• Low corrosion in the environment compared
to metals
• Generally good solvent resistance
7/20/2015
Chapter 1. Primer/introduction
21
Thermoplastics
• Commodities: 75% of the polymer volume
used is with 4 polymer families, polyethylene,
polystyrene, polypropylene and poly(vinyl
chloride) [low cost]
• Intermediate: higher heat deflection
temperatures
• Engineering plastics: can be used in boiling
water
• Advanced thermoplastics: extreme properties
7/20/2015
Chapter 1. Primer/introduction
22
Thermosets
• High moduli, high flex strengths, high heat
deflection temperatures
• Shape is retained during thermal cycling
• Often made with step/condensation
polymerization systems
• Crosslinking is usually used
7/20/2015
Chapter 1. Primer/introduction
23
7/20/2015
Chapter 1. Primer/introduction
24
Polymerization
Formulation
Fabrication
HOW DO WE MAKE A PART?
7/20/2015
Chapter 1. Primer/introduction
25
Formulation
• Additives are used to modify properties
and/or lower costs
• Additives: heat stabilizer, light stabilizer,
lubricant, colorant, flame retardant, foaming
agent, plasticizer
• Reinforcement: particulate minerals, glass
spheres, activated carbon, fibers
• Blends, alloys, laminates
7/20/2015
Chapter 1. Primer/introduction
26
Additives can change:
•
•
•
•
Processing properties
Performance properties
Composites: polymers with fiber fillers
Packaging: multiple layers often used
7/20/2015
Chapter 1. Primer/introduction
27
Formulation operations
• Thermoplastics: melting or solvent processing
• Thermosets: additive addition to monomers
or to prepregs
7/20/2015
Chapter 1. Primer/introduction
28
Fabrication
• Varies by industry sector
– Adhesive
– Coating
– Elastomer
– Plastic
– fiber
7/20/2015
Chapter 1. Primer/introduction
29
Overview of the polymer
industry
Industry
General product requirements
adhesive
Strong surface forces; epoxy, superglue
coatings
Film-forming; LDPE with good impact
composites
Structural materials; epoxy + fibers
elastomers
Large deformation and recovery; rubber in tire and seals
fibers
High strength/area; polyacrylonitrile
foams
Light weight, low thermal conductivity; polyurethane
plastics
Stable deformation under static load; HDPE, PP, PVC
7/20/2015
Chapter 1. Primer/introduction
30
Commodity plastics
Polymer
Major uses
LDPE
Packaging film, wire and cable insulation, toys, flexible bottles,
housewares, coatings
HDPE
Bottles, drums, pipe, conduit, sheet, film, wire and cable
insulation
PP
Automobile and appliance parts, rope, cordage, webbing,
carpeting, film
PVC
Construction, rigid pipe, flooring, wire and cable insulation,
film, sheet
PS
Foam and film packaging, foam insulation, appliances,
housewares, toys
7/20/2015
Chapter 1. Primer/introduction
31
Film blowing
High strength films are achieved by
orienting the crystallites. The film is
biaxially oriented; the wind-up rolls
stretch the film in the machine direction
and the expansion of the film radially
provides a hoop stress force.
7/20/2015
Chapter 1. Primer/introduction
32
Wire coating
Wire coating speeds can be high, and process start-up is challenging. Metal wires may need sizing,
or wetting agents in the polymer melt for good adhesion.
7/20/2015
Chapter 1. Primer/introduction
33
Calendaring
Thin and thick section calendaring is used to make wide sheets (8-12 ft).
7/20/2015
Chapter 1. Primer/introduction
34
Bottle blowing
The parison is inflated,
developing biaxially
orientation similar to that of
blown film. The sides of the
mold provide cooling, quickly
‘freezing’ in the orientation
developed during the
blowing process. When this
process is used to make soda
bottles of PET, the
orientation is critical to
achieving low carbon dioxide
permeation rates (and long
bottle shelf life).
7/20/2015
Chapter 1. Primer/introduction
35
Compression molding
7/20/2015
Chapter 1. Primer/introduction
36
Thermoset applications
Polymer
Major uses
PhenolElectrical equipment, automobile parts, utensil handles,
formaldehyde resins plywood adhesives, particleboard binder
(PF)
Urea-formaldehyde
resins (UF)
Similar to the above; textile coatings and sizings
Unsaturated
polyester (UP)
Construction, vehicle parts, boat hulls, marine accessories,
corrosion-resistant ducts, pipes and tanks, business equipment
Epoxy (EP)
Protective coatings, adhesives, electrical parts, industrial
flooring, highway paving materials, composites
MelamineSimilar to UF resins; decorative panels, counter and table tops,
formaldehyde resins dinnerware
(MF)
7/20/2015
Chapter 1. Primer/introduction
37
Elastomers
• The polymers used for elastomers usually have
very low heat deflection and melt temperatures
• Solids with good mechanical properties are made
by crosslinking polymer chains together
• The “molecular weight” of elastomer parts is the
size of the object
• Vulcanization of rubber uses sulfur to provide
crosslinks between the C=C bonds of natural
rubber.
7/20/2015
Chapter 1. Primer/introduction
38
Fibers
• Fibers are based on highly crystalline polymers
that can be oriented axially to have great
strength. Orientation (cold drawing) develops
crystal structure in the solid.
• Most natural fibers from biomass are based
on cellulose; spider silk has different
compositions and is based on a set of
copolymers
7/20/2015
Chapter 1. Primer/introduction
39
Elastomer polymers
Polymer family
description
Styrene-butadiene
Copolymers with a range of constitutions; SBR – styrenebutadiene rubber
Polybutadiene
Cis-1,4-polymer
Ethylene-propylene
EPD – ethylene-propylene-diene monomer; the small amounts
of diene provide unsaturation
Polychloroprene
Poly(2-chloro-1,3-butadiene); this polar elastomer has excellent
resistance to non-polar organic solvents (gasoline, diesel)
Polyisoprene
Poly(cis-1,4-isoprene); synthetic natural rubber
Nitrile rubber
Copolymer of acrylonitrile and butadiene
Butyl rubber
Copolymer of isobutylene and isoprene
Silicon rubber
Rubber based on polysiloxanes
Urethane rubber
Elastomer with polyethers linked via urethane groups
7/20/2015
Chapter 1. Primer/introduction
40
Synthetic fibers
Fiber type
description
Cellulosic
acetate rayon
Cellulose acetate
viscose rayon
regenerated cellulose
Non-cellulosic
Polyester
Mostly poly(ethylene terephthalate)
Nylon
Nylon 6,6; nylon 6, nylon 10; other aliphatic, aromatic
polyamides
Olefin
Polypropylene; copolymers of vinyl chloride + acrylonitrile, vinyl
acetate, vinylidene chloride
Acrylic
> 80% acrylonitrile; modacrylic = acrylonitrile + vinyl chloride or
vinylidene chloride
7/20/2015
Chapter 1. Primer/introduction
41
Coatings
• Coatings. Major area for expansion; solar cells,
windows, … Supplier base is highly
fragmented.
• Paints. Major area for expansion; vehicles,…
Materials supplier base is clustered; painting
systems base is clustered; user base is
fragmented
7/20/2015
Chapter 1. Primer/introduction
42
Adhesives
• Highly fragmented market
• Value-added!
7/20/2015
Chapter 1. Primer/introduction
43
Foams
• Major area: insulation
for housing, sound
control,…
• Materials:
polystyrene,
polyurethanes, …
• Reaction injection
molding example
7/20/2015
Chapter 1. Primer/introduction
44
Composites
• Thermosets and thermoplastics
• Sheet molding compounds
• Filament winding
7/20/2015
Chapter 1. Primer/introduction
45
Polymer nomenclature is widely varied.
Trademarks and common names may be industry-sector specific.
Nomenclature: Polymer Handbook. Chapter 1.
HOW DO WE NAME POLYMERS?
7/20/2015
Chapter 1. Primer/introduction
46
Source-based names
• Source-based name when the polymer is derived
from a single (original or hypothetical) monomer;
or random co-/ter-polymers
–
–
–
–
Poly(vinyl alcohola)
Poly(styrene-co-butadiene)
Polyformaldehyde (not polyoxymethylene)b
Poly(ethylene oxide) (not poly(ethylene glycol)b
a–
when the name is long, parentheses are used to
separate the name from ‘poly’
b - actually the second name is quite common
7/20/2015
Chapter 1. Primer/introduction
47
Structure-based names
• Structure-based name when the
constitutional repeating unit (CRU) has several
components
• The CRU is independent of the monomers and
polymerization methods
– Poly(hexamethylene adipamide)
– Poly(ethylene terephthalate)
7/20/2015
Chapter 1. Primer/introduction
48
copolymers
Type
Connective
Example
unspecified
-co-
Poly(A-co-B)
statistical
-stat-
Poly(A-stat-B)
random
-ran-
Poly(A-ran-B)
alternating
-alt-
Poly(A-alt-B)
periodic
-per-
Poly(A-per-B-per-C)
block
-block- (-b-)
Poly(A-b-B) or Poly A-block-poly B
graft
-graft- (-g-)
Poly(A-g-B) or Poly A-graft-poly B
7/20/2015
Chapter 1. Primer/introduction
49
Source-based name
Structure-based name
Trade name, abbreviation
polyethylene
polymethylene
PE, LDPE, HDPE, LLDPE
polypropylene
Poly(propylene)
PP
polyisobutylene
Poly(1,1-dmethylethylene)
PIB
polystyrene
Poly(1-phenylethylene)
Styron, Styrofoam
Poly(vinyl chloride)
Poly(1-chloroethylene)
PVC
Poly(vinylidene chloride)
Poly(1,1-dichlorethylene)
Saran
polytetrafluoroethylene
Poly(difluoromethylene)
Teflon
Poly(vinyl acetate)
Poly(1-acetoxyethylene)
PVAC
Poly(vinyl alcohol)
Poly(1-hydroxyethylene)
PVAL
Poly(methyl methacrylate)
Poly(1-methoxycarbonyl-1methylethylene)
PMMA; Lucite, Plexiglass
polyacrylonitrile
Poly(1-cyanoethylene)
PAN; Orlon, Acrilan fibers
polybutadiene
Poly(1-butenylene)
BR rubber
polyisoprene
Poly(1-methyl-1-butenylene)
NR rubber
polychloroprene
Poly(1-chloro-butenylene)
Neoprene
7/20/2015
Chapter 1. Primer/introduction
50
Polymers with other
backbones
Source-based name
Structure-based name
Trade name, abbreviation
polyformaldehyde
Poly(oxymethylene)
POM
Poly(ethylene oxide)
Poly(oxyethylene)
PEO
Poly(ethylene glycol adipate)
Poly(oxyethylene oxyadipoyl)
Polyester 2,6
Poly(ethylene terephthalate)
Poly(oxyethylene oxy-terephthaloyl)
PET; Dacron
Poly(hexamethylene
adipamide)
Poly(iminoadipoyl imino-hexamethylene) Nylon 6,6
Poly(e-caprolactam)
Poly(imino[1-oxohexamethylene])
Nylon 6
polyglycine
Poly(imino[1-oxoethylene])
Nylon 2
7/20/2015
Chapter 1. Primer/introduction
51
Bonding along the backbone is not extraordinary.
With long chains, secondary valence forces, integrated over the entire
chain, provide considerable ‘bonding’ forces.
Chain entanglements provide physical linkages.
WHY ARE LONG CHAIN MOLECULES
SOLIDS?
7/20/2015
Chapter 1. Primer/introduction
52
Chemical bonding in
polymers
•
•
Most primary bonds along the
backbone are covalent
Secondary valence bonds
–
–
–
–
7/20/2015
Much smaller forces than the
covalent bonds, but become
significant when integrated over the
entire chain
Consider the forces acting on this
macromolecule as it is ‘pulled’
through the tube surrounding its
structure in three dimensional space
As each chain segment moves, it
must overcome the local
interactions at the tube surface
Longer chains will have more
resistance to motion
Chapter 1. Primer/introduction
53
Secondary valence forces
• Secondary valence forces affect the glass transition, the
melting temperature, crystallinity, melt flow,…
• They include: nonpolar dispersion, polar dipoles, polar
induction, and hydrogen bonds
Secondary bond
7/20/2015
Bond energy,
kcal/mol
Range of action,
Angstrom
Dispersion
0.1-5.0
3-5 (r-6)
Dipole-dipole
0.5-5.0
1-2 (r-3)
Dipole-induced
dipole
0.05-0.5
1-2 (r-6)
Hydrogen bond
1.0-12
2-3 (r-2)
Chapter 1. Primer/introduction
54
Few synthetic polymers are monodisperse, i.e., have one chain length.
Many biological polymers do have specific molecular weights, e.g., proteins,
DNA, …
The molecular weight distribution has critical effects on polymer properties
in the melt and solid states.
WHAT ARE TYPICAL CHAIN LENGTH
DISTRIBUTIONS?
7/20/2015
Chapter 1. Primer/introduction
55
Typical effects of molecular weight
distributions
• Homopolymers with different molecular weight distributions may be
insoluble in each other
# carbon atoms
State
Use
1-4
Gas
Gaseous fuel
5-11
Low viscosity liquid
gasoline
9-16
Medium viscosity
liquid
kerosene
16-25
High viscosity liquid
Oil, grease
25-50
Crystalline solid
Paraffin wax
1000-3000
Plastic solid
(crystalline +
amorphous)
polyethylene
7/20/2015
Chapter 1. Primer/introduction
Linear
alkane
properties
56
MWD - oligomer
• Poly(a-olefin); PAO6
• Synthetic base oil –
vehicle use
• Trimer, tetramer,
pentamer, hexamer,
heptamer
• Based on 1-decene
• Ionic polymerization
• Differential distribution
by size exclusion
chromatography
• PeakFit™ used for curve
deconvolution
7/20/2015
Chapter 1. Primer/introduction
57
Two polyethylenes
•
•
•
•
•
•
Weight frequency, differential
distributions
Number-average molecular
weights are the same
Weight-average molecular
weights are different
Narrow MWD – PD ~ 5.7
Broad MWD – PD ~ 15
Differences in flow, tensile and
appearance properties
7/20/2015
ån × M
=
ån
i
Mn
i
i
i
åw × M ån × M
=
=
w
å
ån × M
i
i
Mw
i
i
2
i
i
i
i
i
i
i
i
Mw
PD =
Mn
Chapter 1. Primer/introduction
58
In-class exercise
HOW DOES CHAIN LENGTH AFFECT
PROCESSING?
7/20/2015
Chapter 1. Primer/introduction
59
In-class exercise
HOW DOES CHAIN LENGTH AFFECT
PERFORMANCE?
7/20/2015
Chapter 1. Primer/introduction
60
Thermal properties are often key criteria used to select polymers for specific
applications.
Five regions of viscoelastic behavior (many polymers have all five): < glass
transition, power law region, rubbery plateau, rubbery flow, fluid flow
Other – crystalline solids, crosslinked elastomers
WHAT ARE IMPORTANT THERMAL
TRANSITIONS?
7/20/2015
Chapter 1. Primer/introduction
61
Five regions of viscoelasticity
•
•
•
•
7/20/2015
Use amorphous polymers below Tg
Use crystalline polymers below Tm
Crosslinked elastomers at G
Melt processing between B and C
Chapter 1. Primer/introduction
62
Typical G vs T plots
7/20/2015
Chapter 1. Primer/introduction
63
regions
• Viscoelasticity: most polymers creep(slow flow) under long-term stress.
Creep may not be recoverable, i.e., the sample may not recoil to its
original dimensions. Over short periods of time, polymers are elastic.
• Solid yield and fracture: elasticity for e < 0.1%; PS is brittle and fails at low
elongations. PE yields, and then undergoes cold drawing to > 300%
elongation.
7/20/2015
Chapter 1. Primer/introduction
64
BUILDING A GLOSSARY
7/20/2015
Chapter 1. Primer/introduction
65
Medical applications are a
rich applications area for
polymers.
Local variations in surface
roughness at the nanoscale
can induce strains in cell
membranes, leading to the
growth of F-actin stress
fibers that span the length
of the cell.
W.E. Thomas, D. E. Discher, V. P. Shastri,
Mechanical regulation of cells by materials
and tissues, MRS Bulletin, 35 (2010), 578583.
POLYMER SCIENCE DIRECTIONS
7/20/2015
Chapter 1. Primer/introduction
66
Cells feel their environment
• Tissues are hydrated natural polymers with controlled
elasticity
• Most animals cells require adhesion to a solid to be
viable
• Tissue elasticity (~ kPa’s) is important for regulating cell
growth, maturation and differentiation. Brain – 0.2 < E <
1 kPa; fat – 2 < E < 4 kPa; muscle – 9 < E < 15 kPa;
cartilage – 20 < E < 25; bone – 30 < E < 40 kPa
• Nanoroughness seems to affect a number of cell
processes
• 3D scaffolding is important
• Mechanotransduction: cells adhere to surfaces via
adhesive proteins attached to adaptor proteins, to the
actomyosin cytoskeleton.
7/20/2015
Chapter 1. Primer/introduction
67
Fibronectin
Fibronectin plays a major role in
cell adhesion, growth, migration
and differentiation, and it is
important for processes such as
wound healing and embryonic
development.[1] Altered fibronectin
expression, degradation, and
organization has been associated
with a number of pathologies,
including cancer and fibrosis.[2]
7/20/2015
Fibronectin is a high-molecular weight
(~440kDa) glycoprotein of the extracellular
matrix that binds to membrane-spanning
receptor proteins called integrins.[1] In
addition to integrins, fibronectin also binds
extracellular matrix components such as
collagen, fibrin and heparan sulfate
proteoglycans (e.g. syndecans).
Fibronectin exists as a protein dimer,
consisting of two nearly identical monomers
linked by a pair of disulfide bonds.[1] The
fibronectin protein is produced from a
single gene, but alternative splicing of its
pre-mRNA leads to the creation of several
isoforms.
Chapter 1. Primer/introduction
68
Lysozyme models
FIG. 1. Structural models of lysozyme. a
Atomistic model. b Residue
model.
7/20/2015
Chapter 1. Primer/introduction
69
FIG. 3. Graphical elucidation for different
parts of lysozyme.
7/20/2015
Chapter 1. Primer/introduction
70
FIG. 7. Configurations of
lysozyme orientation on a
negatively charged
surface. The direction of
normal to surface is noted
as n and the direction of
dipole of lysozyme is noted
as m . a Side-on orientation
cos =−0.4; b
back-on orientation cos
=0.2.
7/20/2015
Chapter 1. Primer/introduction
71
FIG. 9. Configurations
of lysozyme orientation
on a positively charged
surface.
The direction of normal
to surface is noted as n
and the direction of
dipole of lysozyme is
noted as m . a No
adsorption; b upper
back-on
orientation cos
=0.43; c up end-on
orientation cos
=0.73; d bottom
end-on orientation cos
=−0.81; e lower
back-on orientation
cos =0.26.
7/20/2015
Chapter 1. Primer/introduction
72
Polymer literature is
growing at a rate of
5.7% per year.
SciFinder Scholar (ACS) – chemistry-based
EI Compendex – engineering-based
POLYMER SEARCHES: ELECTRONIC
DATABASES
7/20/2015
Chapter 1. Primer/introduction
73
Case study: Polyethylene
• https://scifinder.cas.org/scifinder/view/scifind
er/scifinderExplore.jsf
• Search by:
– References
– Substances
– reactions
7/20/2015
Chapter 1. Primer/introduction
74
references
Search type
result
Research topics
polyethylene
591,104
Author name
Billmeyer
49 authors;
Company name
Dow (Dow + Dow Corning)
51,887
Document identifier
NA
44,073
Journal
Journal of Applied Polymer
Science
5,801
Patent
Patent number, assignee
name, inventor name,
publication year
Tags
7/20/2015
Chapter 1. Primer/introduction
75
Substance searches
Search type
Chemical structure
result
Draw the structure
Markush
Molecular formula
(C2 H4)n
26997-62-6, poly(ethylidene)
(C H2)n
25038-57-5
Poly(methylene)
property
95 C < boiling point < 120 C
96,994
Substance identifier
polyethylene
9002-88-4 (74-85-1 monomer)
Ethene, homopolymer; 272,891
A monomer-based polymer formula can be:
a single-component homopolymer enclosed by parentheses and followed by either a numeric
repetition or x, as in (C2 H3)x
a multi-component formula enclosed by parentheses and followed by either a numeric repetition or
x, as in (C2 H4 . C Br F3)x
7/20/2015
Chapter 1. Primer/introduction
76
• Analyze:
– Author name, CAS #, CA Section title, company-organization,
database, document type, index term, CA concept heading, Journal
name, language, publication year, supplemental terms
• Refine:
– Research topic, author, company name, document type, publication
year, language, database
• Categorize
– Category heading (polymer chemistry), category (polymers,…), index
terms
7/20/2015
Chapter 1. Primer/introduction
77
Reaction structure
• Input intermediates
7/20/2015
Chapter 1. Primer/introduction
78
Polyethylene search:
9002-88-4 CAS Registry #
7/20/2015
Chapter 1. Primer/introduction
79
Exponential growth rates
7/20/2015
Chapter 1. Primer/introduction
80
7/20/2015
Chapter 1. Primer/introduction
81